Primer HC-068

Primer HC-068

Appointment: metal
Packing:
10 kg
25 kg
Color:
Price: 166 RUB/kg.
The number:
Product successfully added!
To order, go to basket
Continue shopping

Description

Features

Application methods

Primer XC-068 is designed to protect metal products, structures and equipment against corrosive effects of alkalis and mineral acids with a multilayer coating at temperatures up to +60°C.

SHELF LIFE

Warranty period of storage of the primer KHS-068 – 6 months from date of manufacture.

STANDARD PRODUCTION

Production of primer KHS-068 is performed on the basis THAT 6-10-820-75

Доставка по СНГ и России

Наименование

Норма по ТУ 6-10-820-75

Цвет пленки

Серый, красно-коричневый

Внешний вид пленки

Однородная поверхность без посторонних включений

Условная вязкость по вискозиметру типа ВЗ-246 с диаметром сопла 4,0 мм при температуре (20±2)ºС, не менее, с

30-70

Время высыхания до степени 3, при температуре (20±2)ºС, ч, не более

1

Прочность пленки при ударе на приборе У-1, см, не менее

50

Массовая доля нелетучих веществ, %, не менее

31-37

Твердость пленки эмали по маятниковому прибору М-3, усл. ед., не менее

0,3

Адгезия пленки, баллы, не более

3

Степень перетира, мкм, не более

50

Эластичность пленки при изгибе, мм     

1

Стойкость системы покрытий на основе грунтовки ХС-068 при температуре (60±2)°C, ч, не менее, к статическому воздействию 25% растворов:

  • азотной кислоты, гидроокиси едкого натра
  • серной кислоты
  • соляной кислоты

 

 

 

12

8

24

Доставка по СНГ и России

Before applying the primer KHS-068 surface must be cleaned of dust, old paint, grease and other contaminants. Purification is carried out sand-blasting or shot-blasting treatment, may be cleaned cord brushes. For degreasing the metal surface is wiped with a rag soaked in white spirit and dry with a cloth.

If the finish is applied immediately after shot blasting (sand blasting) processing, degreasing is not necessary, thus it is recommended to degrease a particularly contaminated sites.

Before use the primer must be mixed until a homogeneous mass. In the case of production necessity, primer can be diluted to working viscosity with solvents R-4 or R-4A.
Prepared Prime coating is applied on the surface of the protected material at ambient temperatures from -10 º C to +30 º C and relative humidity not above 80%.
After drying of the first layer is applied subsequent layers of materials.

Доставка по СНГ и России

Similar products:

Need help?
Professional help
If you have any difficulties, you can contact our specialists:

8 (800) 700-79-72
8 (800) 700-53-88
8 (835-33) 4-76-83

ICQ 281-034-662
ICQ 671-614-398
ICQ 656-767-981

X
X
X
Thanks for the request!
Your order,
expect a call specialist
Well